Super Duplex 32750 in Sheet, Plate, Bar
SPECIFICATIONS: GRADE Super Duplex | UNS S32750 | ASTM/ASME A240 / F55 | Werkstoff 1.4410
Castle Metals are a stockholder of the 32750 duplex alloys in sheet, plate, and round bar with the added capability of cutting processes to meet requirements across a number of industries.
The following are the properties of 32750 super duplex:
- Ferritic-Austenitic stainless steel.
- Excellent corrosion resistance against general corrosion, stress corrosion cracking, corrosion fatigue, pitting, crevice and erosion corrosion and possessing very high mechanical strength properties.
- Good weldability, post weld heat treatment not necessary.
- Max. Temperature for long periods of service: 280°C (536°F) / (300°C/572°F possible for short periods).
- Surface condition for optimum corrosion resistance: pickled or machined.
Application
Components in offshore, waste water, sea water desalination and chemical plants with aggressive chloride-containing media e.g. heat exchangers, compressor and pump components.
TECHNICAL INFO
Chemical Composition (average %)
| C | Si | Mn | Cr | Mo | Ni | Cu | N | PREN |
|---|---|---|---|---|---|---|---|---|
| 0.020 | 0.25 | 0.55 | 25.80 | 3.40 | 7.00 | max. 0.50 | 0.30 | Min. 40 |
Standards
UNS S32750
Hot Forming
Forging
1200 to 950°C / Air cooling
Heat Treatment
Solution annealing:
1150 to 1000°C (2102-1832°F)
Air cooling
Heat Treatment
Solution annealing / quenching:
1100°C (2012°F)
Water , air (thickness below 2mm)
Structure as quenched:
Ferrite + Austenite
Welding
Weldability of super duplex 32750 is good. The welding procedures are similar to those applied for conventional duplex grades. Welding consumables for different welding methods are available.
MECHANICAL PROPERTIES
Condition: solution annealed
| Product | Size mm |
0.2% proof stress N/mm2 min. |
Tensile strength N/mm2 min. |
Elongation A 5 L Q T |
Impact strength (ISO-V) J min. L Q T |
|---|---|---|---|---|---|
| St, Sch | ≤ 160 | 500 | 795 | 25 - – - - | 100 - – - - |
| P | ≤ 75 | 252) 252) - - | 100 60 - - |
St = Bar ,
Sch = Forging,
P = Sheet or plate
L = Longitudinal, Q = Transverse, T = Tangential
1) < 3mm = A80mm specimen
The values for other products and dimensions shall be established by agreement.
HIGHT TEMPERATURE PROPERTIES
Condition: solution annealed/quenched
| 0.2% yield strength N/mm² min. |
Temperature | |||
|---|---|---|---|---|
| 100°C (212°F) | 150°C (302°F) | 200°C (392°F) | 250°C (482°F) | |
| 450 | 420 | 400 | 380 | |
PHYSICAL PROPERTIES
Thermal conductivity at …………….. 20°C (68°F) …………..15.0 …………W/(m.K)
Specific heat at ………………………..20°C (68°F) …………..500 ………….J/(kg.K)
Electrical resistivity at ………………. 20°C (68°F) …………..0.80 …..Ohm.mm2/m
Modulus of elasticity at …………….. 20°C (68°F) …………..200 x 103 …N/mm2
Magnetic properties …………………………………………………magnetic